Copyright © 2023 Maha Chemicals (Asia) Pte Ltd
METAL SOLUTIONS
FS121M
Accessible small frame metal laser sintering system
- Build Size: 120 × 120 × 100mm
- Laser Type: Fiber laser, 1 × 200W
FS301M
High quality and user-oriented machine for Metal AM production
- Build Size: 305 × 305 × 400mm
- Laser Type: Dual CO₂ Laser, 2 × 100W
FS271M
Brings both performance and price advantage
- Build Size: 275 × 275 × 340mm
- Laser Type: Fiber laser, 1 × 500W
FS421M
True manufacturing system capable of continuous production
- Build Size: 400 x 400 x 400mm
- Laser Type: Max. Dual fiber laser, 2 × 500W
POLYMER SOLUTIONS
eForm
Entry level system with all the functionality and power of an industrial level system
- Build Size: 250 × 250 × 320mm
- Laser Type: CO₂ Laser, 1 × 30W
252P Series
Powerful, high temperature industrial 3D printing system
- Build Size: 250 × 250 × 320mm
- Laser Type: Max. CO₂ Laser, 1 × 100W
403P Series
Farsoon's flagship production polymer system
- Build Size: 400 × 400 × 540 or 400 × 400 × 450mm
- Laser Type: Max. CO₂ Laser, 1 × 100W
Flight HT403P Series
Next generation of high-speed plastic laser sintering
- Build Size: 400 x 400 x 540mm or 400 x 400 x 450mm
- Laser Type: Robust Fiber Laser
HT1001P
For intensive manufacturing cycles with little down time between builds
- Build Size: 1000×500×450mm
- Laser Type: Dual CO₂ Laser, 2 × 100W
MATERIAL SOLUTIONS
Polymer Materials
| PS1212-based Powder | Glass Bead Filled | Carbon Fiber Filled | Mineral Fiber Filled | PA11 Powder | PA6 Powder | PPS Powder | TPU Powder | ||||
|---|---|---|---|---|---|---|---|---|---|---|---|
|
|
FS 3300PA |
FS 3300PA-F |
FS 3401GB |
FS 3400CF |
FS 3250MF |
FS 4100PA |
Ultrasint X043 |
Ultrasint X028 |
FS 8100PPS |
FS 1092A-TPU |
FS 1088A-TPU |
|
General Properties |
|||||||||||
|
Bulk Density |
0.48g/cm3 |
0.45-0.55g/cm3 |
0.67g/cm3 |
0.51g/cm3 |
0.55g/cm3 |
0.49g/cm3 |
0.52g/cm3 |
0.52g/cm3 |
0.57g/cm3 |
0.64g/cm3 |
0.46g/cm3 |
|
Part Density |
0.95g/cm3 |
0.96g/cm3 |
1.26g/cm3 |
1.08-1.10g/cm3 |
1.20g/cm3 |
1.03g/cm3 |
1.14g/cm3 |
1.15g/cm3 |
1.28g/cm3 |
1.12g/cm3 |
1.20g/cm3 |
|
Color |
White |
Black |
Gray |
Black |
Light Gray |
White |
Black |
Light Yellow |
Light Yellow |
White |
White |
|
Thermal Properties |
|||||||||||
|
Melting Point (10°C/min) ISO 11357.1:1997/ISO 11357 |
183°C |
179-185°C |
184°C |
184°C |
183°C |
203°C |
225°C |
220°C |
295°C |
169°C |
160°C |
|
Heat Deflection Temp(HDT) @1.82 Mpa ISO 75-2:2003/ GB/T 1040.2-2006 |
83.5°C |
70-85°C |
68.8°C |
72°C |
129°C |
49°C |
93°C |
100°C |
116°C |
N / A |
N / A |
|
Heat Deflection Temp(HDT) @0.45 Mpa ISO 75-2:2003 / GB/T 1040.2-2006 |
146.2°C |
135-155°C |
152.4°C |
168°C |
171°C |
150°C |
191°C |
199°C |
220°C |
N / A |
N / A |
|
Mechanical Properties |
|||||||||||
|
Tensile Strength ISO 527.2: 1993 / GB/T 1040.2-2006 |
46MPa |
40-50MPa |
44MPa |
65-70MPa |
51MPa |
49MPa |
74MPa |
78MPa |
47MPa |
18MPa |
20MPa |
|
Tensile Modulus ISO 527.2:1993 / GB/T 1040.2-2006 |
1602MPa |
1700-1900MPa |
2644MPa |
4700-6500MPa |
6130MPa |
1542MPa |
3457MPa |
3550MPa |
3412MPa |
61MPa |
30MPa |
|
Elongation at Break ISO 527.2:1993 / GB/T 1040.2-2006 |
36% |
5-20% |
9.3% |
3.0-4.0% |
5% |
58% |
4.0% |
13.0% |
3.8% |
276% |
340% |
|
Flexural Strength ISO 178:2001 / GB/T 1040.2-2006 |
46.3MPa |
36-45MPa |
60.3MPa |
94-113MPa |
76MPa |
60MPa |
99MPa |
121MPa |
63MPa |
6.2MPa |
N / A |
|
Flexural Modulus ISO 178:2001 / GB/T 1040.2-2006 |
1300MPa |
1000-1150MPa |
2210MPa |
4500-5600MPa |
4633MPa |
1463MPa |
2842MPa |
3300MPa |
2906MPa |
86MPa |
27MPa |
|
Izod Impact Strength (notched) ISO 180:2000 / GB/T 1843-2008 |
4.9 KJ/m² |
10-24 KJ/m² |
6.6 KJ/m² |
4.3 KJ/m² |
5.59 KJ/m² |
25 KJ/m² |
10.5 KJ/m² |
3.1 KJ/m² |
2.1 KJ/m² |
No Break |
No Break |
|
Izod Impact Strength (unnotched) ISO 180:2000 / GB/T 1843-2008 |
13.2 KJ/m² |
Tbd. |
31.1 KJ/m² |
16 KJ/m² |
20.78 KJ/m² |
No Break |
67.2 KJ/m² |
9.7 KJ/m² |
5.7 KJ/m² |
No Break |
No Break |
Metal Materials
| Titanium | Aluminium | Maraging Steel | Inconel | Stainless Steel | |||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
|
|
FS Ti6AI4V |
FS TA15 |
FS AISi10Mg |
FS 18Ni300 |
FS IN718 |
FS IN625 |
FS GH3536 |
FS 420 |
FS 15-5PH |
FS 17-4PH |
FS 316L |
|
General Properties |
|||||||||||
|
Density (g/cm3) |
≥ 4.40 |
≥ 4.45 |
≥ 2.65 |
≥ 8.00 |
≥ 8.18 |
≥ 8.40 |
≥ 8.30 |
≥ 7.70 |
≥ 7.76 |
≥ 7.70 |
≥ 7.90 |
|
Mechanical Properties (As built) |
|||||||||||
|
Tensile Strength (MPa) ISO6892-1 |
1150±70 |
1150±70 |
1160±70 |
430±70 |
1150±100 |
1100±70 |
1000±70 |
≥ 1100 |
1200±100 |
1050±100 |
6370±50 |
|
Yield Strength (MPa) ISO6892-1 |
1000±50 |
N / A |
270±30 |
1050±100 |
800±70 |
730±70 |
650±70 |
900±100 |
725±100 |
900±100 |
550±50 |
|
Elongation after Fracture (%) ISO6892-1 |
8 ± 2 |
8 ± 2 |
3 ± 1 |
12 ± 3 |
24 ± 4 |
35 ± 5 |
30 ± 5 |
≥ 2 |
16 ± 4 |
16 ± 4 |
34 ± 5 |
|
Hardness HV ISO6507-1 / HRC ISO6508-1 |
360±30 HV5/15 |
N / A |
140±20 HV5/15 |
35±3 HRC |
300±20 HV5/15 |
270±10 HV5/15 |
270±5 HV5/15 |
48±3HRC |
32-37HRC |
N / A |
215±10 HV5/15 |
|
Mechanical Properties (Heat treated) |
|||||||||||
|
Tensile Strength (MPa) ISO6892-1 |
1050±70 |
1100±20 |
350±50 |
1950±100 |
1350±100 |
1050±70 |
725±70 |
1000±100 |
1450±100 |
N / A |
600±50 |
|
Yield Strength (MPa) ISO6892-1 |
950±50 |
1040±20 |
240±30 |
1900±100 |
N / A |
700±70 |
330±70 MPa |
N / A |
1130±100 |
N / A |
N / A |
|
Elongation after Fracture (%) ISO6892-1 |
12 ± 2 |
13 ± 2 |
6 ± 1 |
4 ± 2 |
16 ± 4 |
35 ± 5 |
43 ± 5 |
17 ± 5 |
14 ± 3 |
N / A |
45 ± 5 |
|
Hardness HV ISO6507-1 / HRC ISO6508-1 |
330±30 HV5/15 |
N / A |
75±20 HV5/15 |
53±3 HV5/15 |
430±30 HV5/15 |
N / A |
N / A |
32±4HRC |
≥ 40HRC |
N / A |
190±10 HV5/15 |